Stainless Steel Flux Cored Wire E316LT-1


INTRODUCTION

Aufhauser E316LT-1 is most frequently used for base metals of similar composition such as AISI Types 301, 302, 304, 305 and 308. The 0.04% maximum carbon content allows for increased resistance to inter-granular corrosion and also minimizes carbide precipitation. These wires have been developed for use with 100% CO2 or 80% Ar/20% CO2 shielding gas. The ability of operating over a wide range of current settings permits deposition rates that are nearly 4 times greater than covered electrodes and up to 50% greater than solid MIG wire. Although the cost per pound of Stainless Steel Flux-Cored wires may be more than that of coated electrodes or solid MIG wire, your cost per pound of deposited weld metal is greatly reduced because of the higher deposition efficiency and lower operational costs. The true stainless steel sheath used in manufacturing Aufhauser Flux-Cored Stainless is your guarantee of smooth performance, x-ray quality welds and a beautiful stainless steel bead appearance. Spatter is extremely low and slag is self-peeling.

 

APPLICATIONS

  • Welding similar alloys containing about 2% molybdenum
  • Temperature service applications (molybdenum increases creep resistance at elevated temperatures)

 

GENERAL INFORMATION

Chemical Composition
Carbon Chromium Nickel Molybdenum Manganese Silicon Phosphorus Sulfur Copper Iron
0.04 17.0-20.0 11.0-14.0 2.0-3.0 0.5-2.5 1.0 0.04 0.03 0.5 Rem

 

PHYSICAL and MECHANICAL PROPERTIES
Tensile Strength 70,000 psi
Density --
Elongation, min. % 30

 

SPECIFICATIONS MEET or EXCEED
AWS: A5.22
ASME: SFA 5.22

 

STANDARD SIZES AND DIAMETERS

Diameters: 0.035", 0.045", and 1/16"